Метод изготовления квадратных стальных труб большого диаметра – ЧАСТЬ 2

EN10219 Квадратная полая стальная труба: Углубленное исследование

How to make large diameter square tubes, methods and techniques for making square tubes：

0022 In the above forming production line, the steel pipe passes through the equipment from the coiling mechanism 1 to the weld bead removal mechanism 8. The process is almost the same as that of the traditional single-seam resistance welded round pipe steel pipe manufacturing equipment. The steel plate materials used for this are usually thick hot rolled coils (such as STKR41, 50, и т.п.), and the coil width will limit the maximum diameter of the final product (large diameter rectangular steel pipe) (in the case of single-slit pipes). In the round steel pipe forming process, the thick steel plate (t=16~26m) деформируется при холодной пластической обработке. Следовательно, во время процесса, из-за вышеуказанной деформации, материал подвергается наклепу и остаточным напряжениям, И сталь вызвана высокочастотной волновой сваркой после формирования. Сварочная деформация, чтобы максимально устранить эту проблему, оставьте место на более длинной секции для медленного охлаждения стальной трубы.

[0023] В способе строительства настоящего изобретения, пространство, необходимое для медленного процесса охлаждения вышеупомянутой стальной трубы, или это место, снабжен нагревательным устройством, оснащенным печью 9 который использует ископаемое топливо в качестве источника тепла и имеет большую длину в направлении транспортировки и высокочастотный индукционный нагрев.. Устройство 10. Следовательно, производственную линию можно установить без значительного удлинения всей производственной линии по сравнению с обычным оборудованием. Там, пока нагретая высокочастотной сваркой часть стали еще не остыла, стальная труба транспортируется к нагревательному устройству и нагревается последовательно или постепенно с течением времени. Нагрев материала путем нагрева стали также эффективен для устранения сварочной деформации или остаточных напряжений в стали., поэтому, возможно, потребуется рассмотреть возможность внесения корректировок в нагревательное устройство.. В любом случае, можно ожидать эффекта энергосбережения. Когда высокочастотное нагревательное устройство 10 установлена ​​на передней ступени, а печь для нагрева ископаемого топлива установлена ​​на задней ступени., вышеупомянутый эффект также тот же самый.

Тем временем 2 показано схематическое поперечное сечение, перпендикулярное продольной оси нагревательной печи. 9. На рисунке, 18 поперечное сечение круглой стальной трубы, а также 19 поперечное сечение крестообразной стальной трубы. Направляющие ролики 20 С обеих сторон стальной трубы в печи установлены нижний направляющий ролик и конвейерный ролик., и хотя бы ролик 20 имеет кольцевую поверхность. /охватывать> Предпочтительно, из-за своей клиновидной формы, зона контакта со стальной трубой 18 шире. Внутренняя стенка отопительной печи 9 обычно изготавливается из сложенных друг на друга огнеупорных кирпичей., и верх выгнут. Горелка и вытяжное устройство на рисунке не показаны.. ИНЖИР. 3 представляет собой концептуальную схему поперечного сечения, перпендикулярного осевому направлению устройства высокочастотного индукционного нагрева. 10. На картинке, 1
0025 Если уровень нагрева стальной трубы 18 принимается во внимание
, высокочастотное нагревательное устройство 10 должен быть установлен в передней части процесса нагрева стальной трубы., или А, на основе холодной обработки пластика, и т.п., для формирования периферийной стенки стальной трубы круглого сечения методом горячей штамповки. Его экструдируют со всех сторон, постепенно образуя стальную трубу квадратного сечения.. Стальная пластина остаточного напряжения удаляется., качество улучшено, и он немедленно транспортируется к многоступенчатому роликовому механизму формирования углов. 11 и нагревается почти до точки фазового превращения 3 1 или А
Теплостойкость и средства охлаждения оборудования относительно легко учесть., с тем преимуществом, что его легче защитить, управлять и продлевать срок службы. Таким образом, термообработанная круглая стальная труба

[0026] Рисунок = 2> или как показано на рисунке 7. На рисунке, 18′ представляет собой поперечное сечение стальной трубы, деформированной до слегка квадратной формы.. На рисунке 6, две оси, ортогональные продольной оси стальной трубы, параллельны друг другу. Формирующие ролики 22 и 22′ (параллельно продольной оси стальной трубы) сожмите окружную поверхность круглой стальной трубы с четырех сторон, чтобы придать ее окружной поверхности слегка переплетающуюся форму.. Например, каждый раз он проходит восемь стадий сверху вниз, Лево и право, а затем ему придают форму постепенно приближающегося прямоугольного сечения. Каждый раз сформированная таким образом стальная труба проходит через стол прокатного стана., его угловой радиус уменьшается, и сечение стальной трубы тоже становится меньше, приближается к квадратной форме, что близко к сечению конечного продукта. 0027 На рисунке 7, окружные поверхности, закрепленные по двум осям, перпендикулярным продольной оси стальной трубы и параллельным друг другу, глубоко соединены. Окружная поверхность круглой стальной трубы штампована из четырех частей.. За счет двух участков, где устранено деформационное упрочнение материала., устранены остаточные напряжения и высокочастотные сварочные деформации., другие угловые зоны также не допускаются. Общее остаточное напряжение чрезвычайно мало., а деградация материала вызвана пластической деформацией вследствие термической обработки.. В случае круглых стальных труб, прошедших термическую обработку и холодную пластическую обработку., заштрихованные части — это два формовочных ролика 23 и 23′ которые составляют плоскую поверхность стальной трубы. Вращаясь в направлении, валку можно придать поперечное сечение, постепенно приближающееся к прямоугольной форме. Тем временем 8 представляет собой вид в разрезе квадратной стальной трубы большого диаметра, образованной роликовым механизмом.. Характеристики этой квадратной стальной трубы горячей штамповки следующие:: На первый взгляд, радиус каждого угла чрезвычайно мал. Форма поперечного сечения стальной трубы (перевернутая форма шара)

0028] Согласно вышеуказанному методу, (Стандарты — это повторяющиеся вещи с характеристиками, связанными с разнообразием, в экономической и технологической деятельности.) когда круглая стальная труба формируется в квадратное поперечное сечение, в обычном процессе, круглая стальная труба сначала проходит через калибровочную машину, чтобы получить идеальное поперечное сечение.. тем не мение, в способе настоящего изобретения, стальной материал размягчается во время горячей обработки, что упрощает изготовление, и поскольку оно деформируется, возможна обработка круглых стальных труб с высокой точностью без использования калибровочного станка. (b) При формовке круглой стальной трубы прямоугольного сечения, чтобы получить точную квадратную стальную трубу, температура внешней периферийной стенки круглой стальной трубы должна поддерживаться примерно одинаковой. 7> тем не мение, согласно этому способу настоящего изобретения, вся стальная труба изготовлена ​​из стали А1 или А3. Поскольку он нагревается почти до точки фазового превращения, он легко деформируется, и можно сформировать квадратную стальную трубу с высокой точностью размеров..

(c) Благодаря термической обработке, углы квадратной стальной трубы могут образовывать очень маленький радиус, и момент сопротивления квадратной стальной трубы может быть уменьшен. тем не мение, стальные трубы имеют тенденцию размягчаться. Материал, полученный в результате отжига стали в предыдущем процессе, можно восстановить путем закалки.. тем не мение, необходимо обратить внимание на состояние деформации стальной трубы вследствие закалки. (г) Пространство, необходимое для охлаждения стали после формирования квадратной стальной трубы, может быть сокращено.. , поэтому материал возле угла с меньшей вероятностью испортится. (г) Так как это горячая обработка, энергия привода формовочного роликового механизма значительно меньше, чем при холодной обработке. (е) Поскольку процесс формования прост и не вызывает деформации стальной пластины., деформация стальной трубы произойдет из-за процесса формирования квадратной стальной трубы.. Либо этого не происходит, или это почти не случается. (F) После формирования квадратной стальной трубы, while the heating temperature is high, it can be quickly cooled by evenly blowing cold air or spraying cold water from all sides to reduce the residual stress caused by processing. 0030] (Часть 2) In order to eliminate and repair the cold steel pipe. Due to the residual stress and material deterioration a i=2> caused by plastic processing, the heat treatment temperature of the steel plate should be set higher and the treatment time longer, but this will cause the surface of the steel pipe to be rough. 4>This will reduce the commercial value of the final product, and removing it requires shot blasting, sand blasting, etc. , increase costs, increase conditions. К тому же, the cost and labor required for heat treatment of steel cannot be ignored. К тому же, by setting the heat treatment temperature low, можно предотвратить шероховатость стальной пластины, но отжига материала возле каждого угла квадратной стальной трубы может быть недостаточно.. Следовательно, во втором способе изобретения, ухудшение состояния стального материала в результате холодной обработки вблизи каждого угла считается особой проблемой в случае материалов квадратных стальных труб.. Чтобы восстановить ущерб, требуется локальный обогрев. Обработка производится вблизи запланированных углов окружной стенки круглой стальной трубы..

0031] тем не мение, когда температура нагрева стенки стальной трубы неравномерна
И когда между ними большая разница, это может = 2> Известно, что даже если он установлен в формовочный роликовый механизм квадратного сечения, как показано на рисунке 7, хорошее квадратное сечение получить невозможно 4> Следовательно, в этой реализации В этом методе, периферийная стенка круглой стальной трубы локально нагревается, и А1, например, используется для нагрева всей круглой стальной трубы. >Нагрейте равномерно почти до точки фазового перехода., отрегулируйте степень размягчения двух компонентов для создания периферийной стенки прямоугольной стальной трубы >Наклеп и термообработка плоских материалов для устранения остаточных напряжений.. Равномерную термическую обработку вышеупомянутой круглой стальной трубы можно провести с помощью устройства, показанного на рисунке. 1. тем не мение, нет необходимости повышать температуру термообработки до точки фазового превращения стального материала А3., поэтому пространство, занимаемое оборудованием для термообработки, относительно невелико.. 4 а также 5 представляют собой принципиальные схемы вариантов выполнения устройства локального обогрева вблизи заданного угла периферийной стенки круглой стальной трубы. /охватывать>Так, в этом случае, электричество используется в обоих случаях. Пара высокочастотных нагревательных катушек 24, 24′ соединены с длиной стальной трубы 18 в направлении руки в поперечном сечении, перпендикулярном центральной оси стальной трубы 18, они установлены симметрично относительно указанной оси и 90 градусов друг от друга. Пара катушек 24 и пара катушек 24′ могут быть установлены с небольшим смещением друг от друга в направлении продольной оси катушек.. Стальная труба. На рисунке, заштрихованная область на материале периферийной стенки стальной части трубы указывает на область, где температура особенно повышена из-за местного нагрева. В случае с рисунком 5, частота, подаваемая на катушку 24′ регулируется так, чтобы внутренняя часть стальной трубы могла лучше нагреваться, и формируется квадратная стальная труба. В это время, каждый угол можно деформировать более свободно и без усилий, и форма угла R более острая, что значит получить квадратную стальную трубу.

Источником тепла для локального нагрева периферийной стенки стальной трубы, конечно, может быть горелка, работающая на ископаемом топливе.. Круглая стальная труба после общего и частичного нагрева удерживается в нагретом состоянии с помощью многоступенчатого формовочного роликового механизма прямоугольного сечения. 11 как показано на рисунке. В этом механизме, например, высококачественная прямоугольная стальная труба большого диаметра, как показано на рисунке. 8 постепенно формируется с помощью многоступенчатого формовочного ролика, как показано на рисунке. 6 или рисунок 7. Последующие шаги такие же, как описано в примерах. (Часть 1).

0034] Согласно вышеуказанному методу строительства, (Стандарты — это повторяющиеся вещи с характеристиками, связанными с разнообразием, в экономической и технологической деятельности.) нагрейте круглую стальную трубу до материала стали вблизи точки фазового превращения А3, и провести термообработку с использованием
В это время, оборудование для термообработки может быть уменьшено, но ожидаемый эффект может быть достигнут для того же материала стальной трубы квадратного сечения..
>
и может сэкономить потребление топлива и/или электроэнергии
. (b) Другие эффекты, достигаемые с помощью способа строительства по этому варианту реализации, по существу такие же, как те, которые описаны в варианте реализации. (1).
【0035】
[Эффекты изобретения] Как описано выше, согласно способу строительства настоящего изобретения, можно изготавливать крупные детали, которые, как известно, производятся методом холодной пластиковой обработки.. Формируя максимально острые углы, можно получить высококачественную стальную трубу без разрушения материала. Квадратная сталь большого диаметра со стабильным общим качеством, упрочнение плоских элементов, и отжиг для устранения внутренних напряжений. Ухудшение качества восстанавливается.. Остаточные напряжения устранены ниже допустимого уровня.. Угловые элементы стальной трубы считаются проблемой для прямоугольных стальных труб..

0036 О термической обработке стальных труб
В процессе формования квадратных стальных труб, когда вся стальная труба нагревается, термообработка квадратной стальной трубы
Обеспечивает высококачественные прямоугольные стальные трубы большого диаметра, которые легко поддаются формовке и образуют острые углы.. Можно получить стальные трубы однородного и стабильного качества.. В случае частичного нагрева стальной трубы (хотя вся стальная труба нагревается при низкой температуре), тепловую энергию можно сэкономить по сравнению с тем, что можно достичь. Оборудование для термообработки занимает меньше места. Затраты, необходимые для операций термообработки, могут быть снижены до относительно низких затрат..
0037] Когда электричество используется в качестве источника тепла для оборудования для термообработки, (Стандарты — это повторяющиеся вещи с характеристиками, связанными с разнообразием, в экономической и технологической деятельности.) оборудование, необходимое для нагрева объекта до необходимой температуры. /охватывать> занимает меньше места. (b) Легко контролировать температуру нагреваемого объекта., а также (c) можно получить продукт стабильного качества. (г) Никакого обслуживания оборудования не требуется. (е) Минус – высокие счета за электроэнергию.. (F) В зависимости от местоположения, общий капитал сообщества может быть не освоен, а необходимое количество электроэнергии может отсутствовать. Другими словами, условия локации ограничены.

[0038] Стоимость термообработки ниже при использовании ископаемого топлива в качестве источника тепла.. Относительно легко получить и транспортировать в больших количествах., независимо от условий сайта. При необходимости могут быть построены объекты большой мощности потребления., но недостаток в том, что отопительные сооружения занимают много места. Если оборудование для термообработки включено последовательно, длина линии формования стальных труб будет значительно увеличена, поэтому важен выбор места размещения оборудования и необходимо сужение ширины. Если принять во внимание вышеупомянутые преимущества и недостатки использования электроэнергии и ископаемого топлива, и внедрить комбинированный метод отопления с использованием электричества и ископаемого топлива., по сравнению с традиционно известными нагревательными печами, возможность установки высокопроизводительного оборудования для термообработки, способного дополнять недостатки друг друга . и т.п., он производит особые функции и эффекты, которых нельзя ожидать при использовании известных методов строительства.. . Контролировать необходимую температуру нагрева довольно сложно..